TILE ADHESIVE - TILE JOINTS - BUILDING MORTAR

KKS® TILEBOND C2-CGI

Price: Contact us

PRODUCT DESCRIPTION
KKS® TILEBOND C2-CGI is one component, cement-polymer based, ready-mixed tile adhesive and grout 2 in 1.
This product meets the technical requirements of C2 class cementitious tile adhesive mortar - high-grade cementitious tile adhesive mortar according to TCVN 7899-1:2008 (or ISO 13007-1: 2004) and meets the technical requirements of CGI grouts and adhesives according to TCVN 7899-3:2008 (or ISO 13007-3: 2004) 
ADVANTAGE
•    High impact resistance: reduce damage to tile caused by impact. 
•    Tile adhesive and Grout 2 in 1, high adhesive strength.
•    Increased polymer helps to minimize peeling and problems in application. 
•    Resistant to vibration and structural movement.
•    Long-time workability, which allows adjustment after applying. 
•    Modified cement-polymer based tile adhesive mortar, with economic efficiency
USES
•    Can be used for both porous tiles and non-porous tiles.
•    To tile the floor, rooftop, terrace.
•    Grouting the decorative tiles and heat-insulating panels.
•    It can be used on horizontal and vertical applications.
APPLICATION
SURFACE PREPARATION
Concrete surface must be clean, sound, level and uncontaminated by oil or grease. Absorbent substrates must be pre-wetted to saturated surface dry condition.
MIXING
The mixing ratio is about 26-28% compare to the amount of mortar.
Mixing the product by trowel until the mixture is consistency. In larger quantities, use the low speed mixer. 
COVERAGE
 About 8.0 kg/m2
APPLYING
Using specialized towel to apply a thin coat, then apply the bond with suitable thickness.
The consumption depends on the surface roughness and the roughness of substrate as well as on the size of the tiles and the placing technique (simple placing or back-buttering).
CLEANING
Clean tools and equipment immediately after finishing work and before the material becomes harden with clean water.
PRODUCT AND TECHNICAL DATA

Form

A mixture of cement - polymer with selective aggregates and additives.

Color

Grey powder

Packaging

25 kg/bag

Density

≈ 1.60 kg/l (bulk density of powder)

≈ 1.90 kg/l (density of fresh mortar)

Mixing ratio

 Water/ Powder = 26-28% (part by weight)

Consumption

1 bag yields approx. 14.5 litters of mortar

69 bags (25kg) for 1m3 of mortar

Adhesion strength in standard condition (after 28 days)

≥ 1.0 N/mm2 (TCVN 7899-2:2008)

Adhesion strength after water immersion (at 28 days age)

≥ 1.0 N/mm2 (TCVN 7899-2:2008)

Adhesion strength after heat aging

(at 28 days age)

≥ 1.0 N/mm2 (TCVN 7899-2:2008)

Resistance to depth abrasion

< 2000 mm3 (TCVN 7899-4:2008)

Flexural strength (after 28 days)

> 2.5 N/mm2 (TCVN 7899-4:2008)

 Compressive strength (after 28 days)

> 15 N/mm2 (TCVN 7899-4:2008)

Shrinkage after 28 days

< 3mm/m (TCVN 7899-4:2008)

Water absorption afer 30 minutes

< 5 g (TCVN 7899-4:2008)

Water absorption afer 240 minutes

< 10 g (TCVN 7899-4:2008)

Initial setting time

> 240 minutes

Pot life

60 minutes (65% r.H, at 27oC)

Adjustment allowance time

20 minutes

Application temperature

8 - 40oC

STORAGE / SHELF LIFE
KKS® TILEBOND C2-CGI must be stored in dry, covered place. Unpacked, undamaged packaging has 9 months of shelf life.
SAFETY INFORMATION
KKS® TILEBOND C2-CGI contains cement which can cause skin irritation. Wear eye protection and respirator. The product is not dangerous when transported. Non-toxic, non-flammable. Dispose of in accordance with local regulations. For more information, please refer to the latest Product Safety Data Sheet.